Kriss Holdings Pvt Ltd


4 X 6m Tarpaulin Sheets




Our company packs the entire range of products with superior-grade packaging material that is nontoxic and recyclable. Furthermore, the packaging prevents damage and ensures the product is kept safe. We are immensely recognized for delivering the orders within the stipulated time frame and at desired Kowloon(Hong Kong).

Material :

  • Material for the plain sheet - Woven high-density polyethylene (HDPE) black fibers fabric laminated on both sides with white low density polyethylene (LDPE) coating.
  • Material for the reinforced attachment points - 6 bands of 7.5cm width made of woven black HDPE fibers fabric and coated with grey LDPE on the outside.
  • Pre-punched 8mm holes on the 2 side bands at 0.1m +/- 10% intervals, positioned in the centre of the bands (only the reinforcement bands are pre-punched, not the tarpaulin itself).


Strength at state of origin and after UV exposure :

  • Tear strength in plain sheet at state of origin - Minimum 100N under ISO 4674-1 2003, strip of 200x200mm, in p lain sheet
  • Tensile strength in Plain sheet at state of origin - Minimum 500N and 15% to 25% elongation in warp and weft in p lain sheet under ISO 1421-1.
  • UV resistance of the p lain sheet,  measured as remaining tensile strength after UV exposure - The tarpaulin tensile strength under ISO 1421-1 after  1500 hours UV under ASTM G53/94 (UVB 313 nm peak)  must be - Minimum 80% of the original value of the actual To be tested in the plain sheet. product, AND not less than 475N.
  • Tensile strength in the reinforcement bands at state of origin - Minimum 700N inside the reinforcement bands as per ISO 1421-1, pulling lengthwise in a p re-punched hole of 8mm with a hook of 8mm wire diameter. To test in 2 holes in each side bands
  • UV resistance of the reinforcement bands measured as remaining tensile strength after UV exposure - The reinforcement bands tensile strength under ISO 1421-1 after 1500 hours UV under ASTM G53/94 (UVB 313 nm peak) must be - Minimum 80% of the original value of the actual product, AND not less than 665N.
  • Welding number and strength at state of origin - Only one welding allowed, in the middle of the sheet, length wise. The tarpaulin tensile strength crossway s at the p lace of the welding under ISO 1421-1 must be - Minimum 50% of the original value of the actual product, AND not less than 400N.


Details :

  • Size, weight, colour, fire resistance
  • Width 4 m ± 1% net width
  • Length 6m minimum net length.
  • Weight, plain sheet only , excluding the bands weight : Min 190g/m² under ISO 3801 +-10% tolerance
  • Weight, complete sheet including bands weight. : Plain sheet specific weight plus 10% additional weight for the reinforcement bands under ISO 3801.